| TYPICAL PROPERTIES OF TOYOLAC 100G-30 |
| Typical
Properties |
|
Test
Method |
|
Test
Conditions |
|
Unit |
|
Typical
Value |
| Melt
Flow Rate |
|
ISO
1133 |
|
240
oC/10kg |
|
g/10min |
|
17 |
| Charpy
Impact, notched |
|
ISO
179 / 1eA |
|
23oC |
|
kJ/m2 |
|
5 |
| Deflection
Temperature Under Load |
|
ISO
75 |
|
120oC/hr,
1.8MPa |
|
oC |
|
103 |
| Tensile
Yield Stress |
|
ISO
527 |
|
5 mm/min |
|
MPa |
|
107 |
| Tensile
Elongation |
|
ISO
527 |
|
5 mm/min |
|
% |
|
>2 |
| Tensile
Modulus |
|
ISO
527 |
|
1 mm/min |
|
MPa |
|
9600 |
| Flexural
Stress |
|
ISO
178 |
|
2 mm/min |
|
MPa |
|
174 |
| Glass
Content |
|
Toray
Method |
|
|
|
wt.% |
|
30 |
| Density |
|
ISO
1183 |
|
|
|
kg/m3 |
|
1260 |