| TYPICAL PROPERTIES OF TOYOLAC 100 X01 |
| Typical
Properties |
|
Test Method |
|
Test Conditions |
|
SI Unit |
|
Typical Value |
| Physical |
| Specific Gravity |
|
ASTM D792 |
|
|
|
- |
|
1.04 |
| Water Absorption |
|
ASTM D570 |
|
23oC
x 24 hours |
|
% |
|
0.3 |
| Mould Shrinkage |
|
ASTM D955 |
|
|
|
% |
|
0.4 ~ 0.6 |
| Rheological |
| Melt Flow Rate |
|
ISO 1133 |
|
220oC
/ 10 kg |
|
g/10 min |
|
15 |
| Mechanical |
| Tensile stress
at yield |
|
ASTM D638 |
|
at 5 mm/min |
|
MPa |
|
41 |
| Tensile strain
at break |
|
ASTM D638 |
|
at 5 mm/min |
|
% |
|
40 |
| Flexural
Strength |
|
ASTM D790 |
|
at 3 mm/min |
|
MPa |
|
63 |
| Flexural Modulus |
|
ASTM D790 |
|
at 3 mm/min |
|
MPa |
|
1960 |
| Rockwell
Hardness |
|
ASTM D785 |
|
R scale |
|
- |
|
105 |
| Impact |
| Izod Impact
Strength, notched |
|
ASTM D256 |
|
12.7 x 62.5 x 12.7tmm
(23oC) |
|
J/m |
|
294 |
| |
|
ASTM D256 |
|
12.7 x 62.5 x 12.7tmm
(0oC) |
|
J/m |
|
196 |
| |
|
ASTM D256 |
|
12.7 x 62.5 x 12.7tmm
(-30oC) |
|
J/m |
|
137 |
| Izod Impact
Strength, notched |
|
ASTM D256 |
|
12.7 x 62.5 x 3.2tmm
(23oC) |
|
J/m |
|
314 |
| |
|
ASTM D256 |
|
12.7 x 62.5 x 3.2tmm
(0oC) |
|
J/m |
|
226 |
| |
|
ASTM D256 |
|
12.7 x 62.5 x 3.2tmm
(-30oC) |
|
J/m |
|
157 |
| Thermal |
| HDT (Unannealed)
127 x 12.7 x 12.7tmm |
|
ASTM D648 |
|
1.82 MPa Loading, 18.56
kg/cm2 |
|
oC |
|
91 |
| HDT (Unannealed)
127 x 12.7 x 6.4tmm |
|
ASTM D648 |
|
1.82 MPa Loading, 18.56
kg/cm2 |
|
oC |
|
85 |
| Thermal
Conductivity |
|
ASTM C177 |
|
|
|
W/K.m |
|
0.15 |
| Coefficient of
Linear Thermal Expansion |
|
ASTM D696 |
|
|
|
mm/mmoC |
|
7.6 x 10-5 |
| Flammability |
| Flammability |
|
UL 94 |
|
|
|
- |
|
HB |
| Electrical |
| Specific Surface
Resistivity |
|
ASTM D257 |
|
at 23oC |
|
ohm |
|
>1016 |
| Specific Volume
Resistivity |
|
ASTM D257 |
|
at 23oC |
|
ohm.cm |
|
>1016 |
| Dielectric
Strength |
|
ASTM D149 |
|
Short Time |
|
KV/mm |
|
24 |
| Dielectric
Constant |
|
ASTM D150 |
|
1000 Hz |
|
- |
|
3.1 |
| Power Factor |
|
ASTM D150 |
|
1000 Hz |
|
- |
|
6.5 X 10-3 |