| TYPICAL PROPERTIES OF TOYOLAC 470Y MH1 |
| Typical Properties |
|
Test Method |
|
Test Conditions |
|
SI Unit |
|
Typical Value |
| Physical |
| Specific Gravity |
|
ASTM D792 |
|
|
|
- |
|
1.08 |
| Mould Shrinkage |
|
ASTM D955 |
|
|
|
% |
|
0.6 ~ 0.9 |
| Rheological |
| Melt Flow Rate |
|
ISO 1133 |
|
240oC
/ 10 kg |
|
g/10 min |
|
2 |
| Mechanical |
| Tensile stress
at yield |
|
ASTM D638 |
|
at 5 mm/min |
|
MPa |
|
39 |
| Tensile strain
at break |
|
ASTM D638 |
|
at 5 mm/min |
|
% |
|
20 |
| Flexural
Strength |
|
ASTM D790 |
|
at 3 mm/min |
|
MPa |
|
62 |
| Flexural Modulus |
|
ASTM D790 |
|
at 3 mm/min |
|
MPa |
|
1960 |
| Rockwell
Hardness |
|
ASTM D785 |
|
R scale |
|
- |
|
110 |
| Impact |
| Izod Impact
Strength, notched |
|
ASTM D256 |
|
12.7 x 62.5 x 12.7tmm
(23oC) |
|
J/m |
|
147 |
| Izod Impact
Strength, notched |
|
ASTM D256 |
|
12.7 x 62.5 x 3.2tmm
(23oC) |
|
J/m |
|
167 |
| Thermal |
| HDT (Unannealed)
127 x 12.7 x 6.4tmm |
|
ASTM D648 |
|
1.82 MPa Loading, 18.56
kg/cm2 |
|
oC |
|
110 |
| Flammability |
| Flammability |
|
UL 94 |
|
|
|
- |
|
HB |