| TYPICAL PROPERTIES OF TOYOLAC ASG-20 |
| Typical
Properties |
|
Test Method |
|
Test Conditions |
|
SI Unit |
|
Typical Value |
| Physical |
| Specific
Gravity |
|
ASTM
D792 |
|
|
|
- |
|
1.22 |
| Mould
Shrinkage |
|
ASTM
D955 |
|
|
|
% |
|
0.1
~ 0.3 |
| Rheological |
| Melt
Flow Rate |
|
ISO
1133 |
|
240oC
/ 10 kg |
|
g/10
min |
|
25 |
| Mechanical |
| Tensile
stress at yield |
|
ASTM
D638 |
|
at 5
mm/min |
|
MPa |
|
130 |
| Tensile
strain at break |
|
ASTM
D638 |
|
at 5
mm/min |
|
% |
|
3 |
| Flexural
Strength |
|
ASTM
D790 |
|
at 3
mm/min |
|
MPa |
|
160 |
| Flexural
Modulus |
|
ASTM
D790 |
|
at 3
mm/min |
|
MPa |
|
7500 |
| Rockwell
Hardness |
|
ASTM
D785 |
|
R scale |
|
- |
|
126 |
| Glass
Content |
|
Toray
Method |
|
|
|
Wt% |
|
20 |
| Impact |
| Izod
Impact Strength, notched |
|
ASTM
D256 |
|
12.7
x 62.5 x 12.7tmm
(23oC) |
|
J/m |
|
50 |
| Thermal |
| HDT
(Unannealed) 127 x 12.7 x 6.4tmm |
|
ASTM
D648 |
|
1.82
MPa Loading, 18.56 kg/cm2 |
|
oC |
|
109 |
| Flammability |
| Flammability |
|
UL 94 |
|
|
|
- |
|
HB |